High Speed Steel (HSS) roll has high hardness and abrasive resistance under high temperature. It is made by centrifuge method; the core part is made of nodular cast iron. Through component and heat treatment technique, the hardness in working layer is able to reach 80-85HSC; matrix in martensite contains V, W, Mo compound carbide so as to assure the even hardness and aperture abrasion in working layer. This kind of roller is applicable to finishing rack to expand working period and improve surface quality of rolling materials.
Chemical Composition
Location |
C |
Si |
Mn |
W |
V |
Nb |
Cr |
Ni |
Mo |
Mg |
Working layer |
1.6-2.0 |
0.2-1.0 |
0.3-1.1 |
1.5-2.5 |
4.0-6.0 |
0.5-1.5 |
4.0-8.0 |
0.5-1.5 |
4.0-6.0 |
|
Core part |
3.2-3.6 |
1.9-2.3 |
0.3-0.7 |
|
|
|
≤0.20 |
0.3-0.7 |
0.2-0.5 |
≥0.05 |
Performance and Application
Location |
Hardness(HS) |
Tensile strength(Mpa) |
Elastic modulus(×103Mpa) |
Purpose |
Working Layer |
80-85 |
700-900 |
210-240 |
Working roll for hot rolled strip, finishing rack for altitude pre-finishing and tandem rolled rod |